Cerdur ZTA consists of zirconoxid cerium hardened aluminum oxide ceramic and excels in very low wear and outstanding durability compared to usual ceramic grinding media. It is particularly convincing with the following properties:
- high breaking strength
- very low abrasion
- long service life
Cerdur ZTA with its density of 4.1 g/cm³ can be employed in almost all mill types and application fields. Thanks to its outstanding properties, it achieves optimal grinding and dispersing results in dry and wet grinding applications of the mineral industry as well as in coatings and paints and many more...
The special material structure of Cerdur ZTA also enables employment at higher circumferential speeds. High economic savings can be realized using this grinding tool due to the interesting price.
- 77 %
- 18 %
- 2 %
- 3 %
- 4,1 g/cm³ ( ± 0,1 cm³)
- Bulk density:
- 2,6 kg/l (depending on bead size)
- E modulus (Gpa):
- Vickers hardness (Hv10):
All values given are approximate.
1,0 mm | 1,5 mm | 2,0 mm | 2,5 mm (tolerance: ± 0,2 mm)
Other sizes upon request.
The grinding media are delivered in containers of 25 kg.
The grinding media should be stored in a dry and clean place.